Produced by templated sol-gel method mesoporous nanosized titania powders modified with 3d-metal ions have been characterized by XPS and TPR methods. Metal species formed on the titania surface were investigated. The TPR analysis showed that reduction behaviors of the Mn+/TiO2 were strongly affected by the synthesis method, preparation conditions and interactions between the dopant metal and TiO2 matrix. It was found that Ti–O–M– bonds formation during sol-gel synthesis with applying nonionic triblockcopolymer Pluronic P123 as organic template and calcination at 550 °C promoted high-dispersion states of doped 5 % metals. The XPS and TPR showing dopants exist as divalent and trivalent ions for Mn+/TiO2, where M=Co, Ni, Mn, and as monovalent and divalent ions in the case of Cu/TiO2.
Одержані темплатним золь-гель методом мезопористі нанорозмірні порошки діоксиду титану, модифікованого йонами 3d металів, досліджено методами PФЕС и ТПВ. Встановлено валентний стан йонів металів на поверхні діоксиду титану. Аналіз термопрограмованого відновлення воднем показав, що відновлювальна здатність Mn+/TiO2 залежить від методу синтезу та умов термообробки. Показано, що формування Ti–O–M зв"язків при золь-гель синтезі, присутність нейонного триблоккополімера Pl&uronic P123 як органічного темплату і термообробка при 550°C стабілізують високодисперсний стан металовмісних сполук. Методами PФЕС та ТПВ показано співіснування дво- та тривалентних йонів металів для Mn+/TiO2, де M=Co, Ni, Mn, та моно- і дивалентног&о стану у випадку Cu/TiO2.